CMC VIRTUTE TABULATUM CERAMIC LATERICIUS
Occurrit specificationes GB/T28635-2012 GB/T25993-2010
Flamma retardat, antistatic, altum robur
Nulla deformatio, nulla color, anti-canus
Simple constructione et mundum situs
Princeps temperatus press SMC sheet corona compositorum
Nulla iactura caemento, nulla terendo autocineto
Certified Non Labi Design
bonum permeability
UV resistentia test
Table 3-1 Ultravioler Test Conditions Standard Source Duration Expositionis ASTM G154
Table 3-1 Ultraviolet Test Conditions
Standard |
Source |
Duratlon expositionis |
ASTM G154a(Cycle 1) |
UVA:340nm |
2,160hours |
ASTM G154b(Cycle 1) |
Xenon Arc:340nm |
1,000hours' |
ASTM G154(Cycle 3) c |
UVB: Type313 |
2,160hours |
Proventus summary |
Mediocris Flexurae Fortitudo Ante UV canus (MPa) |
Mediocris Flexurae Fortitudo Post UV canus (MPa) |
Mediocris Flexurae fortitudo propter UV canus (%) (MPa) |
910 |
820 |
10 |
Flamma retardans g rade
Gradus flamma retardans est FV0, (gradus supremus mateialis non-metallicorum et fumus gradus emissionis 15 in calidis temperaturis combustus est. Fumus est non-toxicus, et gradus ttoxicitatis ZA1 est, qui tutus ievel unus censetur.
Occurrit specificationes ofGB/T28635-2012 GB/T25993-2010
Tertia Pars Testis Corpora: LLOYDS BRITANNICAE, ICAS, SGS
Product Code |
DIMENSIONES (MM) |
ALTITUDO ( MM) |
Pondus (kg) |
Loading (KN) |
DZ1001 |
600X600 |
40 |
6 |
30 |
TS2001 |
400X200 |
30 |
4.8 |
10 |