CMC HIGH STRENGTH FLOOR CERAMIC BRICK

The high-strength wall bricks originated from Europe are made of a composite material. The surface of the product is beautiful, there are different optional colors, and the surface is designed to be non-slip. Aging resistance, high temperature resistance, cold winter resistance, no deformation in harsh environments, no green moss, no broken when rolled by cars, patented design structure. AVATARSMC floor brick technology is at the international leading level, the product fills the international gap, the installation is simple and convenient, the sediment in the ground will not be lost, and the ground will be kept firm. High-strength ceramic tiles are suitable for sponge city construction, and can quickly absorb rainwater in rainy days.

Availability:



Inquire PDF Export

Product Description

CMC HIGH STRENGTH FLOOR CERAMIC BRICK

Meet the specifications of GB/T28635-2012 GB/T25993-2010
Flame retardant, antistatic, high strength
No deformation, no discoloration, anti-aging
Simple construction and clean site
High temperature press SMC sheet molding compounds
No loss of mortar, no crushing by car
Certificated Non-Slip Design
Good permeability

UV resistance test

Table 3-1 Ultravioler Test Conditions Standard Source Duration of Exposure ASTM G154

Table 3-1 Ultraviolet Test Conditions

Standard	Source	Duratlon of Exposure
ASTM G154a(Cycle 1)	UVA:340nm	2,160hours
ASTM G154b(Cycle 1)	Xenon Arc:340nm	1,000hours
ASTM G154(Cycle 3)c	UVB:Type313	2,160hours

Results summary

Average Flexural Strength

Before UV aging

(MPa)

Average Flexural Strength

After UV aging

(MPa)

Average Flexural Strength due to

UV aging(%)

(MPa)

910

820

10

The loss of flexural strength was measured to be approximately 10%

Flame retardant grade

The flame retardant grade is FV0,(the highest grade of non-metallic mateials），and the smoke emission level is 15 when burned at high temperatures.The smoke is non-toxic,and the ttoxicity level is ZA1,which is considered safe ievel one.